Process for integration of a high dielectric constant gate insulator layer in a CMOS device

ABSTRACT

A CMOS device structure, and a method of fabricating the CMOS device, featuring a gate insulator layer comprised of a high k metal oxide layer, has been developed. The process features formation of recessed, heavily doped source/drain regions, and of vertical, polysilicon LDD spacers, prior to deposition of the high k metal oxide layer. Removal of a silicon nitride shape, previously used as a mask for definition of the recessed regions, which in turn are used for accommodation of the heavily doped source/drain regions, provides the space to be occupied by the high k metal oxide layer. The integrity of the high k, gate insulator layer, butted by the vertical polysilicon spacers, and overlying a channel region provided by the non-recessed portion of the semiconductor substrate, is preserved via delayed deposition of the metal oxide layer, performed after high temperature anneals such as the activation anneal for heavily doped source/drain regions, as well as the anneal used for metal silicide formation.

BACKGROUND OF THE INVENTION

[0001] (1) Field of the Invention

[0002] The present invention relates to methods used to fabricate semiconductor devices, and more specifically to a method used to integrate a gate insulator layer, comprised of a high dielectric constant (high k), material, into a CMOS device process sequence.

[0003] (2) Description of Prior Art

[0004] The advent of micro-miniaturization, or the ability to fabricate semiconductor devices with sub-micron features, has allowed device performance, as well as processing costs, to be reduced. The use of sub-micron features has resulted in reductions in performance degrading parasitic capacitances, while a greater amount of smaller semiconductor chips, comprised with sub-micron features, can now be obtained from a specific size substrate, thus reducing the processing cost for a specific semiconductor chip. The continuous scaling down of device dimensions necessitates the use of thinner gate insulator layers, and as the thickness of silicon dioxide layers used as a gate insulator layer decreases, integrity and leakage concerns, not present for gate insulator layers comprised of thicker silicon dioxide layers, become evident. The use of high k dielectric layers as gate insulator layers allow thicker layers to be used, with the thicker, high k dielectric layer supplying capacitances equal to thinner silicon oxide layers, or with the high k dielectric layer having an equivalent oxide thickness (EOT), equal to the thinner silicon dioxide counterpart layer. Therefore the use of high k dielectric layers, for gate insulator layer, will offer reduced leakage when compared to the thicker silicon dioxide gate insulator counterparts.

[0005] Metal oxide layers, such as aluminum oxide (Al₂O₃), zirconium oxide (ZrO₂), and hafnium oxide (HfO₂), are examples of high k dielectric layers, attractive as gate insulator layers for sub-micron devices, however the thermal stability of the metal oxide layers can be a problem when a gate metal insulator is formed prior to subsequent processing steps such as source/drain activation anneals, and metal silicide formation. The temperatures reached during these procedures can result in crystallization of the high k, metal oxide layer, resulting in undesirable gate leakage or shorts. This invention will describe a novel process procedure, and device structure, in which a high k, metal oxide layer is used as the device gate insulator layer, however formed and defined after high temperature anneals, and silicide formation procedures. Prior art, such as Wu, in U.S. Pat. No. 5,972,762, as well as Cha, in U.S. Pat. No. 5,970,329, describe methods of forming recessed elements in metal oxide semiconductor field effect (MOSFET), devices, however these prior arts do not describe the novel device process sequence, and novel process structure, illustrated in this present invention in which a device gate insulator layer, comprised of a high k, metal oxide layer, is integrated into a CMOS device process sequence after high temperature processes have been completed.

SUMMARY OF THE INVENTION

[0006] It is an object of this invention to fabricate a complimentary metal oxide semiconductor (CMOS) device featuring a high k dielectric layer for use as a gate insulator layer.

[0007] It is another object of this invention to integrate a high k, metal oxide, gate layer, into a CMOS fabrication sequence, after high temperature source/drain anneals, and high temperature metal suicide layer formation procedures, have been performed.

[0008] It is still another object of this invention to form the high k, metal oxide gate layer in a space surrounded by lightly doped source/drain (LDD), silicon spacers, wherein the space was created by removal of a silicon nitride masking shape, which in turn is used to define recessed source/drain regions as well as to define word lines.

[0009] In accordance with the present invention a method of integrating the formation of a high k, gate insulator layer into a CMOS fabrication procedure, at a stage of the CMOS fabrication procedure after which high temperature procedures have already been performed, is described. After formation of an N well, and of a P well region, for accommodation of P channel (PMOS), and N channel (NMOS), devices, a silicon nitride shape is formed on the surface of the well regions and used as a mask to selectively remove, and recess, unprotected silicon regions. Heavily doped P type, and N type, source/drain regions are then formed in the recessed portions in the P and N well regions, via ion implantation and annealing procedures, used to activate the implanted ions. Deposition of in situ doped polysilicon layers, and dry etching procedures, result in the formation of P type, and N type, lightly doped source/drain (LDD), spacers, on the sides of the silicon nitride shapes, as well as on the sides of the non-recessed silicon shapes, underlying the silicon nitride masking shapes. Metal silicide regions are next formed in portions of both the P type, and N type heavily doped source/drain region, via formation of a metal shape followed by anneal procedure. After formation of a planarizing insulator layer, the silicon nitride shapes are removed, exposing the surrounding LDD spacers, and exposing underlying non-recessed silicon, located between he heavily doped source/drain regions. A high k, metal oxide layer is deposited, filling the space vacated by the silicon nitride shape, followed by deposition of a conductive layer. Patterning procedures are used to define a conductive gate structure, overlying the high k, metal oxide gate insulator layer. Deposition of, and planarization of, an overlying insulator layer, is followed by definition of contact openings in the insulator layer, exposing portions of top surfaces of the recessed, highly doped source/drain regions, as well as portions of the top surface of the conductive gate structures. Deposition of, and patterning of, a metal layer, results in creation of metal contact and interconnect structures located in the contact openings.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] The object and other advantages of this invention are best described in the preferred embodiments with reference to the attached drawings that include:

[0011] FIGS. 1-19, which schematically, in cross-sectional style, describe key stages of fabrication used to integrate the formation of a high k, gate layer into a CMOS fabrication procedure, at a stage of the CMOS fabrication procedure at which high temperature procedures, such as source/drain anneal, and metal silicide formation, have previously been performed.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0012] The method of forming a complimentary metal oxide semiconductor (CMOS) device featuring a high k, gate insulator layer, integrating into the CMOS fabrication procedure after high temperature procedures, such as source/drain anneal, and metal silicide formation, have previously been performed, will now be described in detail. Semiconductor substrate 3, comprised of single crystalline P type silicon, featuring a <100> crystallographic orientation, is used and schematically shown in FIG. 1. Region 1, of semiconductor substrate 3, will be used for accommodation of P channel metal oxide semiconductor (PMOS), devices, while region 2, will be used for accommodation of N channel metal oxide semiconductor (NMOS), devices. Insulator filled, shallow trench isolation (STI), region 4, is formed in a top portion of semiconductor substrate 3, featuring formation of a shallow trench shape in semiconductor substrate 3, accomplished via photolithographic and dry etching procedures, followed by filling of the shallow trench shape with a silicon oxide layer, in turn obtained via low pressure chemical vapor deposition (LPCVD), or plasma enhanced chemical vapor deposition (PECVD), procedures, using tetraethylorthosilicate (TEOS), as a source. Removal of portions of the silicon oxide layer from the top surface of semiconductor substrate 3, is selectively accomplished via chemical mechanical polishing (CMP) procedures. A photoresist shape, (not shown in the drawings), is used to block out PMOS region 1, from a procedure used to form P well region 5, in NMOS region 2. This is accomplished via implantation of boron, or BF₂ ions, at an energy between about 150 to 250 KeV, at dose between about 1E13 to 1E14 atoms/cm². After removal of the photoresist shape used to protect PMOS region 1, from P well implantation procedures, another photoresist shape, (not shown in the drawings), is used to protect NMOS region 2, from implantation of arsenic or phosphorous ions, implanted at an energy between about 300 to 600 KeV, and at a dose between about 1E13 to 1E14 atoms/cm², allowing formation of N well region 6, to be formed in PMOS region 1. After removal of the NMOS region 2, photoresist block out shape, an anneal procedure is performed at a temperature between about 700 to 1000° C., employed to activate the implanted ions in both well regions. The result of these procedures is schematically shown in FIG. 1.

[0013] Silicon nitride layer 7 a, is next deposited via LPCVD or PECVD procedures, at a thickness between about 10 to 500 Angstroms. If desired a composite layer, comprised of the silicon nitride layer on an underlying silicon oxide layer, can be use in place of silicon nitride layer 7 a. Photoresist shapes 8, each comprised with a width or diameter between about 1000 to 5000 Angstroms, are next formed on silicon nitride layer 7 a. This is schematically shown in FIG. 2. An anisotropic RIE procedure, using CF₄ or Cl₂ as an etchant, is first used to define silicon nitride shapes 7 b, using photoresist shapes 8, as a mask. The anisotropic RIE procedure is then continued, using Cl₂ or SF₆ as an etchant for silicon, to selectively remove portions of semiconductor substrate 3, not protected by photoresist shapes 8, or occupied by STI region 4, creating recessed regions 9, in both PMOS region 1, and in NMOS region 2. The depth of recessed regions 9, in semiconductor substrate 3, is between about 100 to 100,000 Angstroms. This is schematically shown in FIG. 3. Photoresist shapes 8, are then removed via plasma oxygen ashing and careful wet cleans.

[0014] The formation of heavily doped P type, and N type source/drain regions, in the recessed regions of semiconductor substrate 3, is next addressed, and schematically described using FIGS. 4-5. Photoresist shape 10, is used as to protect NMOS region 2, from implantation of boron or BF₂ ions, used to form heavily doped P type source/drain region 11, in a top portion of recessed regions 9, or N well region 6, located in PMOS region 1. The implantation procedure is performed at an energy between about 1 to 50 KeV, at a dose between about 1E12 to 5E12 atoms/cm². After removal of photoresist shape 10, via plasma oxygen ashing, photoresist block out shape 12, is defined, protecting PMOS region 1, from implantation of N type ions, used to from heavily doped source/drain region 13, in a top portion of recessed region 9, or in P well region 5, located in NMOS region 2. Formation of heavily doped N type source/drain region 13, is accomplished via implantation of arsenic or phosphorous ions, at an energy between about 10 to 150 KeV, at a dose between about 1E12 to 1E16 atoms/cm² After removal of photoresist shape 12, via plasma oxygen ashing procedures, an anneal procedure is performed at a temperature between about 500 to 1100° C., for a time between about 0 to 240 min, for purposes of activated the implanted ions in both heavily doped source/drain regions. The anneal procedure can be performed using either conventional furnace, or rapid thermal anneal procedures. In addition the ion activating anneal procedure can be performed after deposition of a subsequent silicon oxide layer, or the activation of the implanted ions can occur during the deposition of the subsequent silicon oxide layer.

[0015] Silicon oxide layer 14, shown schematically in FIG. 6, is next deposited via LPCVD or PECVD procedures, at a thickness between about 50 to 10,000 Angstroms, using a deposition temperature between about 300 to 700° C. Photoresist shape 45, is then employed as a masking shape, allowing the portions of silicon oxide layer 14, to be entirely removed in PMOS region 1. This is schematically shown in FIG. 7. Removal of exposed portions of silicon oxide layer 14, is accomplished either via wet etch procedures using a buffered hydrofluoric (BHF), or a dilute hydrofluoric (DHF), acid as etchant, or via an isotropic dry etch procedure, using CHF₃ as an etchant. Photoresist shape 45, is then removed again via use of plasma oxygen ashing procedures.

[0016] Polysilicon, or silicon layer 15, is next deposited via LPCVD procedures at a thickness between about 100 to 5000 Angstroms. Polysilicon layer 15, is in situ doped during deposition via the addition of diborane to a silane ambient. Polysilicon layer 15, directly interfaces the sides of the silicon nitride shape 7 b, as well as the sides of the non-recessed portion of semiconductor substrate 3, in PMOS region 1, while silicon oxide layer 14, prevents direct overlay of polysilicon layer 15, to silicon nitride shape 7 b, and to the non-recessed portion of semiconductor substrate 3, located in NMOS region 2. After deposition of polysilicon layer 15, silicon oxide layer 16, is deposited via LPCVD or PECVD procedures, at a thickness between about 50 to 10,000 Angstroms. The result of these depositions is schematically shown in FIG. 8. Photoresist shape 17, is next defined and used as an etch mask to protect PMOS region 1, from etching procedures used to remove exposed portions of silicon oxide layer 16, polysilicon layer 15, and silicon oxide layer 14, located in NMOS region 2. This is accomplished via isotropic RIE procedures using CHF₃ as an etchant for silicon oxide layer 16, and silicon oxide layer 14, while Cl₂ or SF₆ is used as an etchant for polysilicon layer 15. This is schematically shown in FIG. 9. Removal of photoresist shape 17, is accomplished via plasma oxygen ashing procedures.

[0017] The removal of the silicon oxide and P type, in situ doped polysilicon from NMOS region 2, allows polysilicon layer 18, to now be deposited and to directly interface the sides of silicon nitride shape 7 b, as well as the sides of the non-recessed portion of semiconductor substrate 3, located in NMOS region 2. Polysilicon layer 18, schematically shown in FIG. 10, is obtained via LPCVD procedures at a thickness between about 50 to 10,000 Angstroms, and is in situ doped via the addition of arsine, or phosphine, to a silane ambient. N type in situ doped polysilicon layer 18, is separated from underlying elements in PMOS region 1, via silicon oxide layer 16. Photoresist shape 19, is then used as a etch mask to allow portions of P type, in situ doped polysilicon layer 18, as well as the remaining portion of silicon oxide layer 16, to be removed in PMOS region 1. This is accomplished via selective, isotropic dry etch procedures, using Cl₂ or SF₆ as an etchant for exposed regions of N type, in situ doped polysilicon layer 18, while CLIF₃ is used as an etchant for the remaining portion of silicon oxide layer 16. The silicon oxide dry etching phase selectively terminates at the appearance of P type, in situ doped polysilicon layer 15. The result of these selective dry etch procedures is schematically shown in FIG. 11. Photoresist shape 19, is removed via plasma oxygen ashing procedures.

[0018] A critical, anisotropic RIE procedure is next performed, selectively removing portions of P type, in situ doped polysilicon layer 15, located in PMOS region 1, and portions of N type, in situ doped polysilicon layer 18, located in NMOS region 2. This is accomplished using Cl₂ or SF₆ as an etchant, resulting in the formation of P type polysilicon spacers 55, located on the sides of silicon nitride shape 7 b, and on the sides of the non-recessed portion of semiconductor substrate 3, located in PMOS region 1, and resulting in the formation of N type polysilicon spacers 58, located on the sides of silicon nitride shape 7 b, and on the sides of the non-recessed portion of semiconductor substrate 3, located in NMOS region 1. P type polysilicon spacers 55, will function as vertical, P type polysilicon, lightly doped source/drain (LDD), elements for the PMOS devices, while N type polysilicon spacers 58, will function as vertical, N type polysilicon, LDD elements for the subsequent NMOS devices. The over-etch cycle, used at the conclusion of the anisotropic RIE procedure used to define the spacers, results in recessing of the spacer structures, now positioned interfacing the center of the sides of silicon nitride shapes. The result of this procedure is schematically shown in FIG. 12.

[0019] Formation of metal silicide layers on portions of both type heavily doped source/drain regions is next addressed and schematically described using FIGS. 13-14. A metal layer, comprised of either titanium, tungsten, tantalum, nickel, or cobalt, is deposited via plasma vapor deposition procedures at a thickness between about 50 to 2000 Angstroms. Photoresist shapes 20, are next formed on the blanket metal layer and used as an etch mask to allow an anisotropic RIE procedure, using Cl₂ as an etchant, to define metal shapes 19, overlying specific portions of the underlying, heavily doped source/drain regions. After removal of photoresist shapes 20, via plasma oxygen ashing, an anneal procedure is used to form metal silicide regions 21, via consumption of portions of the heavily doped source/drain regions. The anneal procedure can be performed using a rapid thermal anneal (RTA) procedure, at a temperature between about 200 to 800° C., for a time between about 0 to 30 min, in an inert ambient, or performed via conventional furnace procedures at a temperature between about 200 to 800° C., for a time between about 0 to 240 min, again performed in an inert ambient. Metal silicide regions 21, are then comprised of titanium silicide, tungsten silicide, tantalum silicide, nickel silicide, or cobalt silicide.

[0020] Insulator layer 22, comprised of a low k layer such as silicon oxide, boro-phosphosilicate glass (BPSG), or phosphosilicate glass (PSG), is next deposited via LPCVD or PECVD procedures, to a thickness between about 1000 to 100,000 Angstroms. A chemical mechanical polishing (CMP), procedure is then used to planarize insulator layer 22, selectively terminating at the appearance of the top surface of silicon nitride shapes 7 b. This is schematically shown in FIG. 15. Silicon nitride shapes 7 b, are now selectively removed via a wet etch procedure, using a hot phosphoric acid solution. If desired silicon nitride shapes 7 b, can be selectively removed via a dry etch procedure, using Cl₂ as a selective etchant for silicon nitride. The removal of silicon nitride shapes 7 b, creates opening 23, exposing the underlying non-recessed portion of semiconductor substrate 3, and located surrounded by the top portions of LDD spacer elements, specifically P type polysilicon spacer 55, in PMOS region 1, and N type polysilicon spacer 58, located in NMOS region 2. This is schematically illustrated in FIG. 16.

[0021] A critical deposition of high k metal oxide layer 24, is next accomplished via metal organic chemical vapor deposition (MOCVD), or via atomic layer chemical vapor deposition (ALCVD) procedures to a thickness between about 10 to 1000 Angstroms, at a temperature between about 100 to 1000° C., using HfCl₄, ZrCl₄, AlCl₃, as reactants for the ALCVD procedure, while using tetrakis dimethyl amino hafnium (TDMAH), or TDMAZ as reactants for the MOCVD procedure. High k metal oxide layer 24, featuring a dielectric constant between about 7 to 500, allows the use of a thicker layer. The higher dielectric constant layer allows an equivalent oxide thickness (EOT), equal to the thinner, lower k dielectric counterparts, to be realized. In addition the increased thickness, acceptable via use of the higher k dielectric layer, reduces the risk of gate insulator leakage or shorts, again when compared to thinner, low k dielectric layers. High k metal oxide layer 24, comprised of aluminum oxide (Al₂O₃), zirconium oxide (ZrO₂), or hafnium oxide (HfO₂), completely fills openings 23, with a portion of the high k dielectric layer residing on the top surface of insulator layer 22. Conductive layer 25, comprised of a metal, or metal silicide layer such as aluminum, aluminum-copper, copper, tungsten, or tungsten silicide, is next deposited on high k dielectric layer 24, via plasma vapor deposition procedures, at a thickness between about 100 to 10,000 Angstroms. If desired conductive layer 25, can be comprised of an in situ doped polysilicon layer. Photoresist shapes 26, are then formed and used as an etch mask to allow an anisotropic RIE procedure, to define the gate, or metal structure 25, as well as removing unprotected portions of high k dielectric layer 24. The anisotropic RIE procedure is performed using Cl₂ as a selective etchant for metal or metal suicide, while RF is used as an etchant for high k dielectric layer 24. The result of this procedure is schematically shown in FIG. 17. Each metal oxide semiconductor field effect transistor (MOSFET), device is now comprised of: lateral, heavily doped source/drain regions; lateral channel regions located in the non-recessed portion of semiconductor substrate 3, underlying a gate dielectric layer comprised of a high k dielectric layer; vertical LDD polysilicon spacers; and a conductive gate structure, self-aligned to the underlying high k dielectric layer.

[0022] After removal of photoresist shapes 26, via plasma oxygen ashing, interlevel dielectric (ILD), layer 27, comprised of either BPSG, PSG, or silicon oxide, is deposited via LPCVD or PECVD procedures, at a thickness between about 100 to 10,000 Angstroms. This is schematically shown in FIG. 18. If desired ILD layer 27, can be subjected to a CMP procedure for planarization purposes. A photoresist shape (not shown in the drawings), is then used as a mask to allow an anisotropic RIE procedure to define contact hole openings 28, exposing portions of top surfaces of metal gate structures 25, as well as metal silicide regions 21, located in PMOS region 1, as well as in NMOS region 2. The anisotropic RIE procedure is performed using CHF₃ as a selective etchant for ILD layer 27, and for insulator layer 22. After removal of the photoresist shape used to define the contact hole openings, a metal layer such as aluminum, aluminum copper, copper, or tungsten, is deposited via plasma vapor deposition procedures, completely filling all contact hole openings, as well as overlying the top surface of ILD layer 27. Another photoresist shape (not shown in the drawings), is formed and used as a mask to allow an anisotropic RIE procedure, using Cl₂ as an etchant, to define metal structures in contact hole openings 28. Metal structures 29 a, 29 b, and 29 c, now communicate with a heavily doped source region, a metal gate structure, and a heavily doped drain region, respectfully, in PMOS region 1, while metal structures 29 d, 29 e, and 29 f, are used for contact to a heavily doped source region, a metal gate structure, and a heavily doped drain region, respectfully, in NMOS region 2. The result of these procedures is schematically shown in FIG. 19. The photoresist shape used to define the metal structures is now removed via plasma oxygen ashing procedures.

[0023] While this invention has been particularly shown and described with reference to the preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit or scope of the invention. 

What is claimed is:
 1. A method of forming a metal oxide semiconductor field effect transistor (MOSFET) device, with a gate insulator layer comprised of a high dielectric constant (high k), dielectric layer, on a semiconductor substrate, comprising the steps of: forming a well region in a top portion of said semiconductor substrate; forming a hard mask on a portion of top surface of said semiconductor substrate; performing a first dry etch procedure to remove a top portion of said semiconductor substrate not covered by said hard mask, resulting in recessed regions in said semiconductor substrate, and a non-recessed portion of said semiconductor substrate covered by said hard mask; forming a heavily doped source/drain region in a top portion of said recessed regions; depositing a polysilicon layer; performing a second dry etch procedure to form lightly doped source/drain (LDD), polysilicon spacers on the sides of said non-recessed portion of said semiconductor substrate; forming a metal silicide region in a top portion of said heavily doped source/drain region; forming a planarized first insulator layer, exposing top surface of said hard mask; removing said hard mask resulting in space located between LDD polysilicon spacers, exposing top surface of underlying said non-recessed portion of said semiconductor substrate; forming said gate insulator layer, comprised of said high k dielectric layer, in said space; and forming a conductive metal structure on said gate insulator layer.
 2. The method of claim 1, wherein said well region is a P well region, obtained via implantation of boron or BF₂ ions, at an energy between about 150 to 250 KeV, at a dose between about 1E13 to 1E14 atoms/cm².
 3. The method of claim 1, wherein said well region is an N well region, obtained via implantation of arsenic or phosphorous ions, at an energy between about 300 to 600 KeV, at a dose between about 1E13 to 1E14 atoms/cm².
 4. The method of claim 1, wherein said hard mask is a silicon nitride shape, formed from a silicon nitride layer, in turn obtained via LPCVD or PECVD procedures, at a thickness between about 10 to 500 Angstroms.
 5. The method of claim 1, wherein the depth of said recessed regions in said semiconductor substrate is between about 100 to 100,000 Angstroms.
 6. The method of claim 1, wherein said heavily doped source/drain region is a P type, heavily doped source/drain region, obtained via implantation of boron or BF₂ ions, at an energy between about 1 to 50 KeV, and at a dose between about 1E12 to 5E15 atoms/cm².
 7. The method of claim 1, wherein said heavily doped source/drain region is an N type, heavily doped source/drain region, obtained via implantation of arsenic or phosphorous ions, at an energy between about 10 to 150 KeV, and at a dose between about 1E12 to 1E16 atoms/cm².
 8. The method of claim 1, wherein said polysilicon layer is a P type in situ doped polysilicon layer, obtained via LPCVD procedures at a thickness between about 100 to 5000 Angstroms, and doped via the addition of diborane to a silane ambient.
 9. The method of claim 1, wherein said polysilicon layer is an N type in situ doped polysilicon layer, obtained via LPCVD procedures at a thickness between about 100 to 5000 Angstroms, and doped via the addition of arsine, or phosphine, to a silane ambient.
 10. The method of claim 1, wherein second dry etch procedure, used to form said LDD polysilicon spacers, is an anisotropic RIE procedure, using Cl₂ or SF₆ as an etchant for said in situ doped polysilicon layer.
 11. The method of claim 1, wherein said hard mask is selectively removed via wet etch procedures using a hot phosphoric acid solution.
 12. The method of claim 1, wherein said hard mask is selectively removed via a dry etch procedure using Cl₂ as an etchant.
 13. The method of claim 1, wherein said high k dielectric layer, used for said gate insulator layer, is comprised of either aluminum oxide (Al₂O₃), zirconium oxide (ZrO₂) or hafnium oxide (HfO₂), obtained at a thickness between about 10 to 1000 Angstroms, via metal organic chemical vapor deposition (MOCVD), or via atomic layer chemical vapor deposition (ALCVD) procedures, performed at a temperature between about 100 to 1000° C., using HfCl₄ or ZrCl₄ as reactants for the ALCVD procedure, or using tetrakis dimethyl amino hafnium (TDMAH), or TDMAZ), as reactants for the MOCVD procedure.
 14. The method of claim 1, wherein said high k dielectric layer is comprised with a dielectric constant between about 7 to
 100. 15. The method of claim 1, wherein said conductive gate structure is comprised of either a metal layer such as tungsten, aluminum, aluminum-copper, or copper, a metal silicide layer such as tungsten silicide, or a doped polysilicon layer.
 16. A method of fabricating a complementary metal oxide semiconductor (CMOS) device on a semiconductor substrate, comprised of a P channel metal oxide semiconductor (PMOS), device, and of an N channel metal oxide semiconductor (NMOS), device, and featuring a gate insulator layer comprised of a high k metal oxide layer formed after completion of high temperature process steps, comprising the steps of: providing a PMOS region in a first area of said semiconductor substrate to be used for said PMOS device, and providing an NMOS region in a second area of said semiconductor substrate to be used for said NMOS device; forming an N well region in a top portion of said PMOS region; forming a P well region in a top portion of said N well region; depositing a silicon nitride layer; performing a first anisotropic RIE procedure to define a silicon nitride shape, and to recess a top portion of said semiconductor substrate, in said PMOS and in said NMOS regions, resulting in a non-recessed portion of said semiconductor substrate, overlaid by said silicon nitride shape, in said PMOS region and in said NMOS regions; performing a first ion implantation procedure to form a P type heavily doped source/drain region in a first recessed region located in said PMOS region; performing a second ion implantation procedure to form an N type heavily doped source/drain region in a second recessed region located in said NMOS region; depositing a first silicon oxide layer; removing portion of said first silicon oxide layer located in said PMOS region; depositing a P type, in situ doped polysilicon layer; depositing a second silicon oxide layer; removing portion of said second silicon oxide layer, portion of said P type, in situ doped polysilicon layer, and portion of said first silicon oxide layer located in said NMOS region; depositing an N type, in situ doped polysilicon layer; removing portion of said N type, in situ doped polysilicon layer and portion of said second silicon oxide layer located in said PMOS region, resulting in a remaining portion of said P type, in situ doped polysilicon layer in said PMOS region, and resulting in a remaining portion of said N type, in situ doped polysilicon layer located in said NMOS region; performing a second anisotropic RIE procedure to form P type polysilicon, lightly doped source/drain (LDD), spacers on the sides of non-recessed portion of said semiconductor substrate and on the sides of a bottom portion of said silicon nitride shape, in said PMOS region, and to form N type polysilicon, LDD spacers on the sides of non-recessed portion of said semiconductor substrate and on the sides of a bottom portion of said silicon nitride shape, in said NMOS region; depositing a first metal layer; performing a patterning procedure to define metal shapes on the top surface of said P type heavily doped source/drain region, and on the top surface of said N type heavily doped source/drain region; performing an anneal procedure to form metal silicide regions in said P type heavily doped source/drain region, and in said N type heavily doped source/drain region; depositing a first insulator layer; performing a chemical mechanical polishing procedure planarizing top surface of said first insulator layer and exposing the top surface of the silicon nitride shapes; removing said silicon nitride shapes resulting in spaces located between polysilicon LDD spacers, exposing the top surfaces of the recessed portions of said semiconductor substrate; depositing said high k metal oxide layer, completely filling said spaces; depositing a second metal layer; performing a third anisotropic RIE procedure to define metal gate structures, and to define gate insulator shape, comprised of said high k metal oxide layer; depositing a second insulator layer; forming contact hole openings in a second insulator layer and in said first insulator layer, exposing portions of top surfaces of said P type heavily doped source/drain region, of said N type heavily doped source/drain region, and of said metal gate structures; and forming metal contact structures in said contact hole openings.
 17. The method of claim 16, wherein said silicon nitride layer is obtained via LPCVD or PECVD procedures, at a thickness between about 10 to 500 Angstroms.
 18. The method of claim 16, wherein the depth of said recess, located in said top portion of said semiconductor substrate, is between about 100 to 100,000 Angstroms.
 19. The method of claim 16, wherein said first ion implantation procedure used to create said P type heavily doped source/drain region, is performed via implantation of boron or BF₂ ions, at an energy between about 1 to 50 KeV, and at a dose between about 1E12 to 5E15 atoms/cm².
 20. The method of claim 16, wherein said second ion implantation procedure used to create said N type heavily doped source/drain region, is performed via implantation of arsenic or phosphorous ions, at an energy between about 10 to 150 KeV, and at a dose between about 1E12 to 1E16 atoms/cm².
 21. The method of claim 16, wherein said P type, in situ doped polysilicon layer is obtained via LPCVD procedures at a thickness between about 100 to 5000 Angstroms, and doped via the addition of diborane to a silane ambient.
 22. The method of claim 16, wherein said N type, in situ doped polysilicon layer is obtained via LPCVD procedures at a thickness between about 100 to 5000 Angstroms, and doped via the addition arsine, or phosphine, to a silane ambient.
 23. The method of claim 16, wherein second anisotropic RIE procedure, used to form said P type polysilicon, LDD spacers and said N type polysilicon, LDD spacers, is performed using Cl₂ or SF₆ as an etchant for polysilicon.
 24. The method of claim 16, wherein said silicon nitride shapes are selectively removed via wet etch procedures using a hot phosphoric acid solution.
 25. The method of claim 16, wherein said silicon nitride shapes are selectively removed via a dry etch procedure using Cl₂ as an etchant.
 26. The method of claim 16, wherein said high k metal oxide layer used for said gate insulator layer is comprised of either aluminum oxide (Al₂O₃), zirconium oxide (ZrO₂), or hafnium oxide (HfO₂), obtained at a thickness between about 10 to 1000 Angstroms, via metal organic chemical vapor deposition (MOCVD), or via atomic layer chemical vapor deposition procedures, performed at a temperature between about 100 to 1000° C., using HfCl₄ or ZrCl₄ as reactants for the ALCVD procedure, or using tetrakis dimethyl amino hafnium (TDMAH), or TDMAZ), as reactants for the MOCVD procedure.
 27. The method of claim 16, wherein said high k metal oxide layer is comprised with a dielectric constant between about 7 to
 100. 28. The method of claim 16, wherein said second metal layer, used for said metal gate structures, is either a tungsten, aluminum, aluminum-copper, or copper layer.
 29. The method of claim 16, wherein said metal gate structures are defined from a metal silicide layer such as tungsten silicide, or from a doped polysilicon layer.
 30. A complimentary metal oxide semiconductor (CMOS), device, featuring a P channel metal oxide semiconductor (PMOS), component in a first region of a semiconductor substrate, and featuring an N channel metal oxide semiconductor (NMOS), component in a second region of said semiconductor substrate, comprising: a P well region located in a top portion of said first region of said semiconductor substrate, and an N well region located in a top portion of said second region of said semiconductor substrate; an insulator filled, shallow trench isolation region, located in a top portion of said semiconductor substrate between said P well region and said N well region; a recessed P well region located in the perimeter of said P well region, with a non-recessed P well portion of said semiconductor substrate located in the center of said P well region, surrounded by said recessed P well region; a recessed N well region located in the perimeter of said N well region, with a non-recessed N well portion of said semiconductor substrate located in the center of said N well region, surrounded by said recessed N well region; a heavily doped P type source/drain region, located in a top portion of said recessed P well region; a heavily doped N type source/drain region, located in a top portion of said recessed N well region; first metal silicide layers located in top portions of said heavily doped P type source/drain region, and second metal silicide layers located in top portions of said N type heavily doped source/drain region; a first metal oxide gate insulator layer located overlying the top surface of said non-recessed P well portion of said semiconductor substrate, and a second metal oxide gate insulator layer overlying the top surface of said non-recessed N well portion of said semiconductor substrate; vertical P type silicon spacers located on the sides of said non-recessed P well portion of said semiconductor substrate, and located on the sides of a bottom portion of a first metal oxide gate insulator layer; vertical N type silicon spacers located on the sides of said non-recessed N well portion of said semiconductor substrate, and located on the sides of a bottom portion of a second metal oxide gate insulator layer; conductive gate structures located overlying the metal oxide gate insulator layers; an interlevel dielectric (ELD) layer located overlying said conductive gate structures; contact hole openings in said ILD layer exposing top surface of said conductive gate structures, and exposing top surface of said heavily doped P type source/drain region, and of said heavily doped N type source/drain region; and metal structures located in said contact hole openings.
 31. The CMOS device of claim 30, wherein the depth of said recessed P well region, located in perimeter of said P well region, and of said recessed N well region, located in perimeter of said N well region, is between about 100 to 100,000 Angstroms.
 32. The CMOS device of claim 30, wherein said vertical P type silicon spacers, and said vertical N type silicon spacers, are comprised of polysilicon.
 33. The CMOS device of claim 30, wherein said metal oxide gate insulator layers are comprised of either aluminum oxide (Al₂O₃), zirconium oxide (ZrO₂), or hafnium oxide (HfO₂), at a thickness between about 10 to 1000 Angstroms, and with said metal oxide gate insulator layers comprised with a dielectric constant between about 7 to
 100. 34. The CMOS device of claim 30, wherein said conductive gate structures are comprised of either tungsten, aluminum, aluminum-copper, copper, tungsten silicide, or doped polysilicon.
 35. A metal oxide semiconductor field effect transistor (MOSFET) device, comprising: a well region located in a top portion of a semiconductor substrate; a recessed well region located in the perimeter of said well region, with a non-recessed well portion of said semiconductor substrate located in the center of said well region, surrounded by said recessed well region; a heavily doped source/drain region located in a top portion of said recessed well region; metal silicide layers located in top portions of said heavily doped source/drain region; a metal oxide gate insulator layer located overlying the top surface of said non-recessed well portion of said semiconductor substrate; vertical silicon spacers located on the sides of said non-recessed well portion of said semiconductor substrate, and located on the sides of a bottom portion of said metal oxide gate insulator layer; a conductive gate structure located overlying said metal oxide gate insulator layer; an interlevel dielectric (ILD) layer located overlying said conductive gate structure; contact hole openings in said ILD layer exposing top surface of said conductive gate structure, and exposing top surface of said heavily doped source/drain region; and metal structures located in said contact hole openings.
 36. The MOSFET device of claim 35, wherein said well region is a P type well region.
 37. The MOSFET device of claim 35, wherein said well region is an N type well region.
 38. The MOSFET device of claim 35, wherein the depth of said recessed well region, located in perimeter of said well region, is between about 100 to 100,000 Angstroms.
 39. The MOSFET device of claim 35, wherein said vertical silicon spacers are comprised of either P type doped polysilicon or of N type doped polysilicon.
 40. The MOSFET device of claim 35, wherein said metal oxide gate insulator layer is comprised of either aluminum oxide (Al₂O₃), zirconium oxide (ZrO₂), or hafnium oxide (HfO₂), at a thickness between about 10 to 1000 Angstroms, and with said metal oxide gate insulator layer comprised with a dielectric constant between about 7 to
 100. 41. The MOSFET device of claim 35, wherein said conductive gate structure is comprised of either tungsten, aluminum, aluminum-copper, copper, tungsten silicide, or doped polysilicon. 